聚丙烯切片样品粒度与用量对其熔融曲线的影响
    点此下载全文
引用本文:
摘要点击次数:  1457
全文下载次数:  468
作者单位
金小培 (中国纺织科学研究院 研究开发中心,北京 100025) 
中文摘要:在差示扫描量热分析过程中,通过改变样品粒度及用量,考查了对聚丙烯切片热行为的影响。结果表明:样品粒度变大或样品用量增加会导致熔融峰顶温度升高,同时会使熔融焓有轻微变化。因此在仪器的灵敏度可满足的情况下,为得到切片真实结晶结构参数的有效方法是减少样品用量(例如5 mg以下)。
中文关键词:聚丙烯  差示扫描量热分析  样品粒度  熔融峰顶温度  熔融热焓值
 
Influence of the Sample Size and Amount on the Melting Curve of Polypropylene Chips
Abstract:Based on the test process of differential scanning calorimetry, the influences of the size and amount of polypropylene chips on thermal behavior are researched. The results show that increasing the sample size or the sample amount will lead to the melting peak temperature increases, while melting enthalpy will have a slight variation. Therefore, in the case that the sensitivity of the instrument can be met for the test's requirement, an effective way to get real crystal structure parameters of the chips is to reduce the amount of sample (for example 5 mg or less).
keywords:polypropylene  differential scanning calorimetry  sample size  melting peak temperature  melting enthalpy
查看全文  查看/发表评论  下载PDF阅读器
版权所有 合成纤维 Copyright©2008 All Rights Reserved
主管单位:上海市纺织控股(集团)公司 主办单位:上海市合成纤维研究所 全国合成纤维科技信息中心
地址:上海市平凉路988号  邮编:200082  电话:021-55216165 55214320  E-mail:hcxwbjb@163.com hcxw@chinajournal.net.cn
技术支持:北京勤云科技发展有限公司